of rhodium was formed, distinguishable by its colour, and by the triple salt it formed with muriate of soda.
To analyse the compound of steel with iridium and osmium, the alloy should be acted on by dilute sulphuric acid, and the residuum boiled in the acid; the powder left is to be collected and heated with caustic soda in a silver crucible to dull redness for a quarter of an hour, the whole to be mixed with water, and having had excess of sulphuric acid added, it is to be distilled, and that which passes over condensed in a flask: it will be a solution of oxide of osmium, will have the peculiar smell belonging to that substance, and will give a blue precipitate with tincture of galls. The portion in the retort being then poured out, the insoluble part is to be washed in repeated portions of water, and then being first slightly acted on by muriatic acid to remove the iron, is to be treated with nitromuriatic acid, which will give a muriate of iridium.
In these analyses, an experienced eye will frequently perceive, on the first action of the acid, the presence of the alloying metal. When this is platinum, gold, or silver, a film of the metal is quickly formed on the surface of the acid.
Of alloys of platinum, palladium, rhodium, and iridium and osmium, a ready test is offered when the point is not to ascertain what the metal is, but merely whether it be present or not. For this purpose we have only to compare the action of the same acid on the alloy and on a piece of steel; the increased action on the alloy immediately indicates the presence of the metal; and by the difference of action, which on experience is found to be produced with the different metals, a judgement may be formed even of the particular one present.
The order in which the different alloys stand with regard to this action is as follows: steel, chromium alloy, silver alloy, gold alloy, nickel alloy, rhodium alloy, iridium and osmium alloy, palladium alloy, platinum alloy. With similar acid the action on the pure steel was scarcely perceptible; the silver alloy gave very little gas, nor was the gold much acted on. All the others gave gas copiously, but the platinum alloy in most abundance.
In connexion with the analysis of these alloys, there are some very interesting facts to be observed during the action of acids on them, and perhaps none of these are more striking