116 STAT. 3202 PROCLAMATION 7529-MAR. 5, 2002 ANNEX (continued) 13 percent transverse, reduction of area 22 percent longitudinal, 6 percent transverse: density of 7.78 Mg/m'; produced in an electric furnace then vacuum arc rc-melt furnace; hot-rolled or forged to shape; age hardened to HRc 45-48; (will) hot-rolled products designated as X-142, known as "SCM 415," with the following chemical composition: carbon, 0.1J - 0.18 percent; silicon, 0.15 - 0.35 percent; manganese, 0.60 - 0.85 percent; phosphorus, equal to or less than 0.03 percent; sulfur, equal to or less than 0.03 percent: chromium, 0.90 - 1.20 percent; molybdenum, 0.15 - 0.30 percent; hardness: HRB of 87; tensile strength of 500 N/mm'; elongation of 30 percent; yield ratio of 80 percent; thickness: 2.6 - 4.0 mm; width: 1066 mm - 1321mm; edge: square cut edge free of burrs, rice marks, protrusions or damage; (xxiv) flat-rolled products (provided for in subheadings 7208.25.30 through 7208.25.60), designated as X-139 or X-087, weighing more than 17.8 kg per mm of width, having a camber tolerance of not more than 25.4 mm per 914.40 cm, a width tolerance of not more than 12.70 mm, and (.A) in thicknesses ranging from 2.03 to 4.57 mm and having a gauge tolerance of+'- 0.05 mm, in widths from 756 to 1410 mm, or (B) in thicknesses ranging from 2.31 to 4.57 mm and having a gauge tolerance of+/- 2 percent, in widths from 775 to 1373 mm, and having a carbon content of 0.001-0.004, or (C) in thickness ranging from 2.03 to 2.92 mm and having a gauge tolerance of+/- 0.05 mm, in widths from 760 to 968 mm, all the foregoing certified by the importer of record to be used for rerolling, and in an aggregate annual quantity not to exceed 750,000 metric tons; (.\\\) blue finish band saw steel meeting the following characteristics: thickness less than or equal to 1.31 mm; width less than or equal to 80 mm; chemical composition: carbon content of 1.2 to 1.3 percent, by weight, silicon content of 0.15 to 0.35 percent, by veig^'; manganese content of 0.20 to 0.35 percent, by weight; phosphorus content less than or equal to 0.03 percent, by weight; sulphur content less than or equal to 0.007 percent, by weight; chromium content of 0.30 to 0.5 percent, by weight; and nickel content less than or equal to 0.25 percent, by weight; with the following other properties: carbides fully spheroidized, having greater than 80 percent of carbides, which are less than or equal to 0.003 mm and uniformly dispersed; surface finish is blue finish free from pits, scratches, rust, cracks, or seams; smooth edges; edge camber (in each 300 mm of length) of less than or equal to 7 mm arc height; and cross bow (per mm of width) of 0.015 mm maximum, the foregoing designated as X-OIO; (x.w i) cold-rolled products designated as X-015, as described below: (A) uncoated flat products, less than 4.75 mm in thickness, not further worked than cold-rolled, comprising either- (I) products known as "Grade C80M" in widths less than 300 mm and thickness greater than 0.25 mm; containing, by weight, 0.70 percent carbon, 0.30 percent silicon, and 0.30 percent manganese and also containing, by weight, 0.03 percent phosphorus, 0.02 percent sulfur, 0.35 percent chromium, 0.10 percent copper, 0.20 percent nickel, 0.02 percent aluminum, 0.001 percent oxide, 0.003 percent titanium and 0.01 percent tin; (!!) products known as "Gradel6MnCrSM2 described in industry usage as of carbon steel, produced in widths less than 300mm and thickness greater than 0.25 mm containing, by weight, 0.11 percent carbon, 0.20 percent silicon, and 0.85 percent manganese and also containing, by weight, 0.02S percent phosphorus and 0.01 percent sulfur with the combination of phosphorous and sulphur not to exceed 0.03 percent, 0.95 percent chromium, 0.15 percent copper, 0.15 percent nickel and 0.08 percent aluminum; or
�
